<ol id="f3lln"><var id="f3lln"><em id="f3lln"></em></var></ol><cite id="f3lln"><dfn id="f3lln"><ruby id="f3lln"></ruby></dfn></cite>

    <em id="f3lln"><dfn id="f3lln"></dfn></em>

<mark id="f3lln"></mark>

<sub id="f3lln"><listing id="f3lln"><meter id="f3lln"></meter></listing></sub><output id="f3lln"></output>

<delect id="f3lln"></delect>

    <font id="f3lln"><sub id="f3lln"></sub></font>
    <noframes id="f3lln">
    <mark id="f3lln"></mark><delect id="f3lln"></delect>

      <b id="f3lln"></b>
        <p id="f3lln"><listing id="f3lln"></listing></p>
        <ruby id="f3lln"><menuitem id="f3lln"><strike id="f3lln"></strike></menuitem></ruby>
            <delect id="f3lln"></delect>
            <b id="f3lln"></b>

              <p id="f3lln"><listing id="f3lln"></listing></p>

                  推荐产品

                  厂址:河南省巩义市新中镇新中村

                  联系人:13598803768窦总

                                 15617556118
                    固话:0371-64337888

                    传真:0371-64337999

                    网址:http://www.labwata.com

                  行业知识

                  宝珠砂在熔模铸造中替代锆砂和锆砂粉的目标

                  2017-10-19 浩洋宝珠砂 1413

                       宝珠砂在熔模铸造中替代锆砂和锆砂粉的目标宝目前,我国熔模精密铸件的年产量在50万吨以上,型壳废料大约在100万吨以上,型壳材料的循环利用,是一项值得关注的重要课题。
                  质量较高的熔模精密铸件,型壳的面层耐火材料(包括涂料中的骨料和撒砂)大都采用锆砂粉和锆砂。铸件脱壳后,无法将其与背层耐火材料分离,不仅浪费了资源短缺、价格高昂的锆砂,而且增加了型壳废料回收利用的难度。
                       我国的宝珠砂是经电熔后制得的,质地致密,表面光滑,性能优于烧结陶粒。特别是制造宝珠砂时,由于喷吹的作用,270目以下的微粒(粒径0.053㎜以下)可能有5%左右。这些微粒,保留在宝珠砂中是不适宜的。如果将其收集,用于配制面层涂料,填充性能一定明显优于经表面熔烧处理的粉料。由此可以看出目前,我国熔模铸造行业中免用锆砂的条件已经具备。 